Stress Corrsion Cracking of Austenitic Stainless Steels in High Temperature Water and Alternative Stainless Steel

Toshio Yonezawa1
1 Tohoku University 6-6-10, Aoba, Aramaki, Aoba-ku, Sendai 980-8579, Japan

Main Article Content

Abstract

In order to clarify the effect of SFE on SCC resistance of austenitic stainless steels and to develop the alternative material of Type 316LN stainless steel for BWR application, the effect of chemical composition and heat treatment on SFE value and SCCGR in oxygenated high temperature water  were studied. The correlation factors between SFE values for 54 heats of materials and their chemical compositions for nickel, molybdenum, chromium, manganese, nitrogen, silicon and carbon were obtained. From these correlation factors, original formulae for SFE values calculation of austenitic stainless steels in the SHTWC, SHTFC and AGG conditions were established. The maximum crack length, average crack length and cracked area of the IGSCC for 33 heats were evaluated as IGSCC resistance in oxygenated high temperature water. The IGSCC resistance of strain hardened non-sensitized austenitic stainless steels in oxygenated high temperature water increases with increasing of nickel contents and SFE values.  From this study, it is suggested that the SFE value is a key parameter for the IGSCC resistance of non-sensitized strain hardened austenitic stainless steels. As an alternative material of Type 316LN stainless steel, increased SFE value material, which is high nickel, high chromium, low silicon and low nitrogen material, is recommendable.

Article Details

References

1) C.F. Cheng, “Intergranular Stress-Assisted Corrosion Cracking of Austenitic Alloys in Water-cooled Nuclear Reactors”, J. Nucl. Mater. 57, p.11-33, 1975.
2) H.H.Klepfer et al. : “Investigation of Cause of Cracking in Austenitic Stainless Steel Pipe”, G.E.Report NEDDO-2100, Vol.I and II, 1975.
3) T.Kondo : “Japanese contributions to fields of predicting and combating environmentally assisted cracking(EAC) of steels in LWR water”, Journal of Nuclear Science and Technology, 26(1), pp.126 - 131, 1989/01.
4) M. Kowaka et al. : “Development of Nuclear Grade Type 316 Stainless Steel for BWR Pipes”, Karyoku Genshiryoku Hatsuden, 32, pp.1303-1315, 1981.
5) ASME Sec.III, 1978.
6) K. Kumagai, S. Suzuki, J. Mizutani, C. Shitara, K. Yonekura, M. Masuda, T. Futami, “Evaluation of IGSCC Growth Behavior of 316NG PLR Pipe in BWR”, PVP-Vol.479, PVP2004-2666, 2004.
7) M.Ueki et al. : “Influence of Stacking Fault Energy on Plastic Flow of Cr-Ni Austenitic Stainless Steels”, Tetsu-to-Hagane, 71, pp.743-748, In Japanese, 1985.
8) E.B.Pickering, “Physical Metallurgical Development of Stainless Steels”, Stainless Steel '84, The Inst. of Metals, p.2, 1984.
9) T. Yonezawa, T. Iwamura, “Metallurgical Study on IGSCC of Non-sensitized Low-carbon 316 Stainless Steel in BWR Environment”, FONTEVRAUD VI, A137, T03, 2006.
10) T. Yonezawa et al. : “Effect of Chemical Compositions on IGSCC Resistance for Strain Hardened Low Carbon Austenitic Stainless Steels in High Temperature Water”, Proceedings of the 14th international conference on Environmental Degradation of Materials in Nuclear Power Systems -Water Reactors-, Virginia Beach, VA, Aug. 23-27, 2009.
11) T.Yonezawa et al. : “The Effect of Chemical Composition and Heat Tratment Conditions on Stacking Fault Energy for Fe-Cr-Ni Austenitic Stainless Steel”, Metallurgical and Materials Transactions A, Vol. 44A, pp.5884-5896, 2013.
12) J.P. Perdew et al. : Phys. Rev. B, vol. 46, pp.6671-6687, 1992.