Research on degradation of silk fibroin by combination of electron beam irradiation and hydrothermal processing
Main Article Content
Abstract
Silk fibers and silk proteins have been demonstrated to be useful to apply in the textile industry, biomedical, cosmetics, pharmaceuticals. In this study, the effects of electron beam (EB) irradiation combined with hydrothermal processing to the solubility of silk fibroin and generation of soluble silk protein were investigated. The solubility of unirradiated and irradiated fibroin samples were greater than 80 % when hydrothermal degradation was performed in the sodium hydroxide solution at an appropriate concentration of 0.05 M. However, the solubility of irradiated fibroin was greater than that of unirradiated sample. The soluble silk protein content increased from 0.462 to 0.653 mg protein/mg silk fibbroin when irradiation doses increased from 0 to 200 kGy, respectively. The molecular weight of protein was determined by SDS-PAGE method. The characteristics of silk protein were confirmed by scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA) and X-ray diffraction (XRD).
Article Details
Keywords
Silk fibroin, silk protein, electron beam irradiation
References
[2] J. Kundu et al., “Silk fibroin nanoparticles for cellular uptake and control release”, International Journal of Pharmaceutics, 388: 242-250, (2010).
[3] A. Sionkowska et al., “The influence of UV radiation on silk fibroin”, Polymer Degradation and Stability, 96: 523-528, (2011).
[4] R. Rajkhowa et al., “Ultra-fine silk powder preparation through rotary and ball milling”, Powder Technology, 185: 87-95, (2008).
[5] GH. Altman et al., “Silk-based biomaterials”, Biomaterials, 24: 401-416, (2003).
[6] A. Kojthung et al., “Effects of gamma radiation on biodegradation of Bombyx mori silk fibroin”, International Biodeterioration & Biodegradation, 62: 487-490, (2008).
[7] Q. Lu et al., “Degradation Mechanism and Control of Silk Fibroin”, Biomacromolecules, 12: 1080-1086, (2011).
[8] K. Kang et al., “Behavior of hydrothermal decomposition of silk fibroin to amino acids in near-critical water”, Korean Journal of Chemical Engineering, 21 (3): 654-659, (2004).
[9] Y. Suzuki et al., “Enzymatic degradation of fibroin fiber by a fibroinolytic enzyme of Brevibacillus thermoruber YAS-1”, Journal of Bioscience and Bioengineering, 108 (3): 211-215, (2009).
[10] RL. Horan et al., “In vitro degradation of silk fibroin”, Biomaterials, 26: 3385-3393, (2005).
[11] W. Lamoolphak et al., “Hydrothermal production and characterization of protein and amino acids from silk waste”, Bioresource Technology, 99: 7678-7685, (2008).
[12] H. Takeshita et al., “Production of fine powder from silk by radiation”, Macromolecular Materials and Engineering, 283 (1): 126-131, (2000).
[13] H. Yamada et al., “Preparation of undegraded native molecular fibroin solution from silkworm cocoons”, Materials Science and Engineering, C 14: 41-46, (2001).
[14] OH. Lowry et al., “Protein measurement with the folin phenol reagent”, Journal of Biological Chemistry, 193(1): 265-275, (1951).
[15] S. Halabhavi et al., “Interaction of 8 MeV Electron Beam with P31 Bombyx mori Silk Fibers”, Materials Sciences and Application, 2: 827-833, (2011).
[1] GM. Nogueira et al., “Preparation and characterization of ethanol-treated silk fibroin dense membranes for biomaterials application using waste silk fibers as raw material”, Bioresource Technology, 101: 8446-8451, (2010).